Ferrosilicon is an iron alloy composed of iron and silicon. Ferrosilicon is an iron-silicon alloy made of coke, steel scraps, quartz (or silica) as raw materials and smelted in an electric furnace.
Â
Â
Grade
|
Chemical Composition (mass fraction)%
|
Si
|
Al
|
Ca
|
Mn
|
Cr
|
P
|
S
|
C
|
≥
|
≤
|
FeSi90Al1.5
|
87.0~95.0
|
1.5
|
1.5
|
0.4
|
0.2
|
0.04
|
0.02
|
0.2
|
FeSi9oAI3.0
|
87.0~95.0
|
3
|
1.5
|
o.4
|
o.2
|
0.04
|
0.02
|
0.2
|
FeSi75AI0.5-A
|
74.0~80.0
|
0.5
|
1
|
o.4
|
l0.3
|
0.035
|
0.02
|
0.1
|
FeSi75AI0.5-B
|
72.0~80.0
|
0.5
|
1
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
FeSi75Al1.0-A
|
74.0～80.0
|
1
|
1
|
0.4
|
0.3
|
0.035
|
0.02
|
0.1
|
FeSi75Al1.0-B
|
72.0~80.0
|
1
|
1
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
FeSi75AI1.5-A
|
74.0~80.0
|
1.5
|
1
|
0.4
|
0.3
|
0.035
|
0.02
|
0.1
|
FeSi75Al1.5-B
|
72.0~80.0
|
1.5
|
1
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
FeSi75Al2.0-A
|
74.0~80.0
|
2
|
1
|
0.4
|
0.3
|
0.035
|
0.02
|
0.1
|
FeSi75AI2.0-B
|
72.0~80.0
|
2
|
—
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
FeSi75-A
|
74.0~80.0
|
—
|
—
|
0.4
|
0.3
|
0.035
|
0.02
|
0.1
|
FeSi75-B
|
72.0~80.0
|
—
|
—
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
FeSi65
|
65.0~72.0
|
—
|
—
|
0.6
|
0.5
|
0.04
|
0.02
|
—
|
Â
Application of Ferrosilico
Â
Ferrosilicon is widely used in steelmaking, cast iron, low carbon
Â
Ferroalloy production:
1. In the field of steelmaking, ferrosilicon is used as a deoxidizer and alloying agent to achieve the purpose of steep and diffusion deoxidation. Adding a certain amount of ferrosilicon to steel can improve the strength, hardness, elasticity and permeability of steel.
2. In cast iron, ferrosilicon is used as a ball grinding agent and an alloying agent, especially in ductile iron. Adding ferrosilicon to cast iron can prevent the formation of carbides and promote the precipitation and spheroidization of graphite. Then the mechanical ability can be the same as steel.
3. High silicon ferrosilicon can be used to produce low carbon reducing agent in ferroalloy industry.
4. In addition, ferrosilicon powder can be used as a suspension phase in the mineral processing industry and as a coating for welding electrodes in electrode manufacturing.